NACERA® BLUE X
TRANSLUCENT LIQUID

blue-x-header.jpg
Blue-X-Stempel.jpg
Innovative. Translucency and color transition in one stroke – simply paint translucency and turn monolithic into a multi-layer
Flexible. Cusp tips and incisal edges — use where desired
Certainty. Increase translucency and keep „full-strength“ mechanical properties
Efficient. Anterior Esthetics at Half the cost – eliminate costly Cubic Zirconia inventory
Indication: Single units and bridges up to 3 units

Blue-x-schritte-1.jpg

Brush

Blue-x-schritte-2.jpg

Sinter

Blue-x-schritte-3.jpg

Glaze

Blue-x-schritte-4.jpg

+8% Translucency

 

We have surpassed Cubic Zirconia in the desire for a strong, but highly translucent and cost effective Zirconia. Nacera’s Blue X, applied to Nacera® Pearl 3Y-TZP Zirconia, exceeds the aesthetic properties of lithium disilicate by allowing technicians to brush the right amount of translucency only where desired. The translucency will increase up to 8% even on shaded Nacera® Zirconia. The advantages continue with improvements in strength. Nacera® Pearl Zirconia treated with Blue X retains its flexural strength of 1.200 MPa, almost double Cubic Zirconia, and up to 3x that of lithium disilicate!

Blue X was especially developed for Nacera® Pearl Zirconia. It will lower the Chroma when applied to Incisal or Occlusal areas and generates a lifelike color transition – creating a brushed Multilayer effect! The concept is unique to „Blue X,“ a world first—made in Germany by DOCERAM Medical Ceramics.

Blue-X-Tabelle-Verlauf.jpg

Nacera® Pearl treated with Nacera® Blue X tested according ISO 6872 can achieve:

Flexural Strength 1.200 MPa
Fracture Toughness >9MPa√ m
Translucency +4% Thickness 1,5 mm
+6% Thickness 1,0 mm
+8% Thickness 0,5 mm